Sichuan Liaofu Special Steel Company is one of the most experienced manufacturers and suppliers of din 1.2767 tool steel flat square bar in China. With over 20 years' experience, our factory offer high quality products made in China with competitive price. Welcome to contact us for wholesale service.
Product Description
Description
DIN 1.2767 Cold Work Tool Steel
Equivalence
AISI / SAE | DIN / W.Nr | JIS | GB |
---- | 1.2767 | SKT6 | ---- |
Chemical Composition (%)
C | Si | Mn | P | S | Cr | Mo | Ni |
0.40 | 0.10 | 0.20 | ≤ | ≤ | 1.20 | 0.15 | 3.80 |
Dimensions
Shape | Thick / Dia. (mm) | Width (mm) |
Round | 8-600 | / |
Flat | 6-200 | 20-900 |
Block | 150-500 | 200-1000 |
Production
Delivery Condition
EAF+LF+VD+(ESR), Hot rolled or Forged, Annealed, Hardness≤285HB, Unmachined or Machined
surface (Peeled, Turned, Grinded), UT 100% Passed
Characteristics
1. Cold work tool steel with high thoughness and full hardenability, also large dimensions.
2. High impact strength and compressive strength.
3. For oil and air hardening.
4. Good polishability.
Applications
For
making the highly stressed coining tools, cutlery dies, hobbing tools,
cold shear blades for heavy gauge material, plastic moulds.
Heat Treatment
Annealing
610 to 650°C
Slow controlled cooling in furnace at a rate of 10 to 20°C/hr down to approx. 600°C,
further cooling in air.
Hardness after annealing: max. 285 HB.
Stress relieving
Approx. 650°C
Slow
cooling in furnace; intended to relieve stresses set up by extensive
machining, or incomplex shapes. After through heating, hold in neutral
atmosphere for 1 to 2 hours.
Hardening
840 to 870°C
Oil, salt bath (300 to 400°C), air. Holding time after temperature equalization: 15 to 30 minutes.
Obtainable hardness:
53 - 57 HRC in air.
54 - 58 HRC in oil or salt bath.
Production
Tempering
Slow
heating to tempering temperature immediately after hardening/time in
furnace 1hour for each 20 mm of work piece thickness, but at least 2
hours/cooling in air. For certain cases we recommend to reduce tempering
temperature and increase holding time.
Production
Finish Product:
UT TEST
For Guarantee Product Quality.
A. Sand Hold Detection;
B. Hardness Detection.
10.Delivery Time
1) For abundant stock, 7-15 days.
2) For customized products, 15-30 days.
Production
Loading Details:
11.FAQ:
Q1: What do you do for the control of the quality?
A1: Before loading into the container, our products will all be inspected by ultrasonic inspection. Quality Grade conforms to SEP 1921-84 E/e, D/d, C/c as per customer's request.
Q2:: What are your hot-selling products?
A2:
D2/1.2379, H13/1.2344, CR12MOV, DC53, CR8, abundant stock for both
plates and rounds. Competitive prices and short lead-time.
Q3: Can we visit your company and factory?
A3:
Yes, warmly welcome! We can book the hotel for you before you come to
China and arrange our driver to our airport to pick you up when you
come.
Q4: Are you a manufacturer or merely a trader?
A4: We
are a group of companies and owned manufacturer bases and trading
companies. We specialized in plastic mold steel, hot work mold steel,
cold work mold steel, alloy steel for mechanical, high-speed steel, etc.
All materials are of high quality and competitive price.
HOR SALE GRADE:
Plastic Mold steel: P20 / NAK80 / 2083R
Cold Work Steel: DC53 / Cr12 / M2 / T1
Hot Worl Steel: H13 / H13R / 1.2344
Alloy Steel: 20Cr / 4140 / SCM440
Carbon steel Stainless: GCr15 / 304 / SUJ420
↓For Details Please Contact Us↓
Hot Tags: din 1.2767 tool steel flat square bar, China, manufacturers, suppliers, factory, D3 Mould Steel Bar, 1 2344 Steel Bar, D3 Mould Square Bar, a2 steel bushcraft knife, 1 2316 Steel Bar, a2 steel heat treating